Wear and friction properties of H-Al-17Si alloy with dry, lubrication and coated (DLC-Star) conditions under HFRR /

Abstract

Dry, lubrication (SAE15W40), and coated (DLC-Star) reciprocating tribological tests on rapid solidified AlSi17Cu3.5-4Mg0.6-0.8 alloy was conducted using a high frequency linear reciprocating rig (HFRR) at ambient temperature. The alloy fabricated with the rheo-stir squeeze casting procedure under T-6 condition. However, at different loading (0-30 N) conditions, wear and friction properties of rapid solidified H-Al-17Si alloy are investigated. It is observed that the lower friction coefficient value obtained for DLC-Star coated H-Al-17Si alloy compared to dry and lubrication conditions. Though, for dry and lubricated sliding, the obtained wear coefficient values are 2.9X10-3 mm3/N.m and 4.0X10-4 mm3/N.m. A lower coefficient of wear value of 5.4X10-5 mm3/N.m was recorded with DLC-star coating under dry conditions. The alloy wear coefficient values first increases with applied load (up to 20 N) and then decreases (20 N to 30 N). EDS, AFM surface roughness profilometer, SEM, and advanced metallurgical microscope (AMM) analysis techniques used for the characterization of surface morphologies. The developments in friction and wear coefficients were fundamentally ascribed to the dispersion and size of primary Si elements and the development of tribo-oxide films on the rapid solidified AlSi17 alloy coated (DLC-Star) surfaces.